Influence of temperature histories during reactor startup periods on microstructural evolution and mechanical properties of austenitic stainless steel irradiated with neutrons

Kasahara, Shigeki; Kitsunai, Yuji*; Chimi, Yasuhiro; Chatani, Kazuhiro*; Koshiishi, Masato*; Nishiyama, Yutaka

Journal of Nuclear Materials, 480, p.386 - 392, 2016/11

https://doi.org/10.1016/j.jnucmat.2016.06.017

This paper addresses influence of two different temperature profiles during startup periods in the Japan Materials Testing Reactor and a boiling water reactor upon microstructural evolution and mechanical properties of austenitic stainless steel irradiated with neutrons to about 1 dpa and 3 dpa. Tensile tests at 290C and Vickers hardness tests at room temperature were carried out, and their microstructures were observed by FEG-TEM. Influence of difference in the temperature profiles was observed obviously in interstitial cluster formation, in particular, growth of Frank loops. The influence was also found certainly in loss of strain hardening capacity and ductility, although the influence on the yield strength and the Vickers hardness was not clearly observed. As a result, Frank loops, which were observed in austenitic stainless steel irradiated at doses of 1 dpa or more, were considered to contribute to deformation of the austenitic stainless steel.